Impact of Process Poisons on the Performance of Post‐Phthalate Supported Ziegler–Natta Catalysts in Gas Phase Propylene Polymerization

Résumé

The impact of common process catalyst poisons on the performance of a 6th generation Ziegler–Natta catalysts during the gas phase polymerization of propylene are examined using two approaches: introducing propylene without purification, or with one or two sets of purification columns, and by introducing carbon dioxide (CO2), oxygen (O2), water (H2O), methanol (CH3OH), ethyl acetate (C4H8O2) and dimethyl sulfoxide (C2H6SO) during the polymerization. As expected, purification columns increases the catalyst activity significantly, slightly reduce catalyst decay. Injecting TiBA during the reaction leads to an activity increase. The addition of two full sets of columns substantially increased the repeatability of polymerization reactions. The power of deactivation of poisons injected during the polymerization reaction is: O2 > CO2 > CH3OH > C2H6SO > C4H8O2 > H2O. Adding CO2, O2, and CH3OH resulted in a progressive decrease in molecular weight while almost no effect is observed with H2O. However, C4H8O2, and C2H6SO resulted in a mild increase in molecular weight. Additionally, the effects on crystallinity and stereoregularity are similar where CO2, O2, H2O and CH3OH caused a progressive decrease while C4H8O2 and C2H6SO resulted in a mild increase, indicating some isotacticity control by these two poisons.
Fichier principal
Vignette du fichier
mren-poisons manuscript draft-Final Revision-Plain.pdf (2.11 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04886638 , version 1 (14-01-2025)

Licence

Copyright (Tous droits réservés)

Identifiants

Citer

Abdulrahman Albeladi, Akhlaq Moman, Timothy F L Mckenna. Impact of Process Poisons on the Performance of Post‐Phthalate Supported Ziegler–Natta Catalysts in Gas Phase Propylene Polymerization. Macromolecular Reaction Engineering, 2022, 17 (4), pp.2200049. ⟨10.1002/mren.202200049⟩. ⟨hal-04886638⟩
0 Consultations
0 Téléchargements

Altmetric

Partager

More