Spectroscopic properties and continuous-wave laser operation of Nd:Ca 0.7 La 0.3 Mg 0.3 Al 11.7 O 19 crystal

Résumé

The polarized absorption spectra, polarized fluorescence spectra and fluorescence decay curve of Nd:Ca0.7La0.3Mg0.3Al11.7O19 (CLnA) crystal were recorded at room temperature. The Judd-Ofelt parameters Ω2, Ω4 and Ω6 were calculated to be 0.80×10−20 cm2, 3.83×10−20 cm2 and 2.71×10−20 cm2, respectively. The spontaneous transition rates, branching ratios and the radiative lifetime were calculated for the 4F3/2 excited state. The emission cross section is 4.01×10−20 cm2 at 1052 nm for σ-polarization and 0.96×10−20 cm2 at 1052 nm for π-polarization, respectively. Continuous-wave (CW) laser operations of a-cut and c-cut Nd:Ca0.7La0.3Mg0.3Al11.7O19 crystals have been demonstrated.
Fichier principal
Vignette du fichier
ome-10-5-1255.pdf (838.4 Ko) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-02613618 , version 1 (01-12-2020)

Identifiants

Citer

Yuxin Pan, Bei Liu, Jian Liu, Qingsong Song, Jie Xu, et al.. Spectroscopic properties and continuous-wave laser operation of Nd:Ca 0.7 La 0.3 Mg 0.3 Al 11.7 O 19 crystal. Optical Materials Express, 2020, 10 (5), pp.1255-1263. ⟨10.1364/OME.389014⟩. ⟨hal-02613618⟩
32 Consultations
54 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More