Microstructural and mechanical characterization of refractories based on Kaolin DD3 and dolomite (5-20% wt) [Elaboration et caracterisation microstructurale et mecanique des refract aires a base de kaolin DD3 et de dolomite (5-20%POIDS)] - Université Claude Bernard Lyon 1 Accéder directement au contenu
Article Dans Une Revue Annales de Chimie - Science des Matériaux Année : 2013

Microstructural and mechanical characterization of refractories based on Kaolin DD3 and dolomite (5-20% wt) [Elaboration et caracterisation microstructurale et mecanique des refract aires a base de kaolin DD3 et de dolomite (5-20%POIDS)]

H. Bounib
  • Fonction : Auteur
H. Osmani
  • Fonction : Auteur
Gilbert Fantozzi
  • Fonction : Auteur
  • PersonId : 883180

Résumé

The east Algerian kaolin DD3 is characterized by its wealth of alumina and its physical and mechanical properties after calcination. The aim of this work is to improve these properties by addition of dolomite to calcined kaolin DD3 (Grog) and to reduce the rate of vitreous phase. The latter is presented in the form of cristobalite between 1100°C and 1400°C and an amorphous phase above 1400°C. An excess of the amorphous phase reduce the creep strength and decrease the thermomechanical properties of the refractory. The mixtures between 5 and 20% weight of dolomite were treated and sintered under the same conditions between 1200°C and 1550°C. The samples are analyzed by XRI), SEM and physical and mechanical measurements. XRD Spectra show that the addition from 5 to 20% weight of dolomite led, after sintering, to form ceramic composite composed mainly of phases: mullite, anorthite, spinel and indialite (cx-cordierite). 1 he addition of dolomite more than 10% reduces the rate of the amorphous phase to 9.6% after sintering in the temperature range 1200°C and 1500°C. Ceramics obtained is characterized by: an apparent density in the range 2,88 to 3,21 g/cm3, a very low porosity, a module of rupture between 67 and 112 MPa and a Vickers microhardness from 9,1 to 10,67 GPa. © Lavoisier, Paris Réfractaires á base de kaolin DD3.

Dates et versions

hal-01854808 , version 1 (07-08-2018)

Identifiants

Citer

H. Bounib, H. Osmani, K. Loucif, Jérome Chevalier, Gilbert Fantozzi. Microstructural and mechanical characterization of refractories based on Kaolin DD3 and dolomite (5-20% wt) [Elaboration et caracterisation microstructurale et mecanique des refract aires a base de kaolin DD3 et de dolomite (5-20%POIDS)]. Annales de Chimie - Science des Matériaux, 2013, 38 (3-4), pp.131-145. ⟨10.3166/acsm.38.131-145⟩. ⟨hal-01854808⟩
33 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More